金属学报(英文版)
Titanium based IrO2 +Ta2O5 oxide anodes with different compositions and pyrolysis temperatures were prepared by termodecompoisition method. By using X-ray diffraction (XRD), the structure and texture coefficient of the coatings, TC(hkl), of IrO2 rutile crystal have been tested. It showed that, the crystallization processes of IrO2 and Ta2O5 in xIrO2 +(100-x) Ta2 O5 (x is in mol%) films affected and confined each other.In the mixed system, IrO2 rutile phase existed as a solid solution with Ta, and attained the maximum solubility when x=70mol%, i.e. for the coating of 70% IrO2 +Ta2O5.For the coatings of low iridium content or at low preparing tem pemture, (110) and (101) pwtered orientations were dominant. However, preferred growth of IrO2 weakened with increasing either iridium content or temperature. Three typical surface morphologies were observed by using scanning electron tnicroscopy(SEM). The crystallite size of the mixed oxide coatings were finest for the the film of 70%IrO2 +30%Ta2O5,and decreased with the pyrolysis tempemture. As the results of the finest crystallite segregating on sudece and the maxitnum solid solubility of Ir and Ta component in deposits, the coatings with the composition of 70%IrO2 +Ta2O5 prepared at 450℃ presented the mdrimutn electrocatalgtic activitg for O2 evolution in 0. 5M H2SO4 solution.UP to 550℃, Ti base suffered to oxidation resulting in decreasing anode conductivity,therefore, coatings performed a low activity.
关键词:
titanium based coating anode
,
null
,
null
,
null
,
null
,
null
J.M. Hu
,
H.M. Meng
,
D.B. Sun
,
S.J. Zhang
,
J.X. Wu and D.J. Yang Beijing Corrosion and Protection Center
,
Open Laboratory of Corrosion
,
Erosion and Surface Technology
,
University of Science and Technology Beijing
,
Beijing 100083
,
China
金属学报(英文版)
Service life of two different oxide anodes in phenolsulfonic acid (PSA) solution was investigated by accelerated electrolysis. The durability of Ti/IrO_2+Ta_2 O_5 anode increased by the addition of SnO_2 in the mixed oxides. The degradation mechanisms of Ti/IrO_2+ Ta_2 O_5 and Ti/IrO_2 +Ta_2 O_5 +SnO+2 anodes were different. It was shown from the observation of scanning electron microscopy (SEM) and the electrochcmical measurement that, the deactivation of Ti/IrO_2 + Ta_2 O_5 anode was due to the build-up of an organic film on surface. The growth of the covered film on surface was restricted by addition of SnO_2, which resulted in increasing of the service life of anodes. The over-potential for oxygen evolution on Ti/IrO_2 +Ta_2 O_5 electrode increased after doping SnO_2, and the intermediate products of PSA building-up on the surface was much more rapidly oxidized. Meanwhile, a certain part of the surface oxide deposit entered into the solution leading to loss of oxides, which resulted in degradation of Ti/IroO_2 + Ta_2 O_5 anode containing SnO_2 component.
关键词:
metal oxide anode
,